OBJECTIVES: The purpose of this study was to evaluate the antimicrobial activity of an acrylic resin combined with an antimicrobial polymer poly (2-tert-butylaminoethyl) methacrylate (PTBAEMA) to inhibit Staphylococcus aureus, Streptococcus mutans and Candida albicans biofilm formation. MATERIAL AND METHODS: Discs of a heat-polymerized acrylic resin were produced and divided according to PTBAEMA concentration: 0 (control), 10 and 25%. The specimens were inoculated (10(7) CFU/mL) and incubated at 37ºC for 48 h. After incubation, the wells were washed and each specimen was sonicated for 20 min. Replicate aliquots of resultant suspensions were plated at dilutions at 37ºC for 48 h. The number of colony-forming units (CFU) was counted and expressed as log (CFU+1)/mL and analyzed statistically with α=.05. RESULTS: The results showed that 25% PTBAEMA completely inhibited S. aureus and S. mutans biofilm formation. A significant reduction of log (CFU+1)/mL in count of S. aureus (control: 7.9±0.8A; 10%: 3.8±3.3B) and S. mutans (control: 7.5±0.7A; 10%: 5.1±2.7B) was observed for the group containing 10% PTBAEMA (Mann-Whitney, p<0.05). For C. albicans, differences were not significant among the groups (control: 6.6±0.2A; 10%: 6.6±0.4A; 25%: 6.4±0.1A), (Kruskal-Wallis, p>0.05, P=0.079). CONCLUSIONS: Acrylic resin combined with 10 and 25% of PTBAEMA showed significant antimicrobial activity against S. aureus and S. mutans biofilm, but it was inactive against the C. albicans biofilm.

Polymethyl methacrylate (PMMA) resins have commonly been used as a denture base material. However, denture bases may act as a reservoir for microorganisms and contribute to oral diseases in denture wearers. It is hypothesized that the 2-tert-butylaminoethyl methacrylate (TBAEMA) incorporated to acrylic resins should have antimicrobial activity related to the presence of amino groups on acrylic resin surface. OBJECTIVES: The objectives of this study were to evaluate the presence of amino groups on acrylic resin surface and the influence on flexural strength after incorporation of TBAEMA. MATERIAL AND METHODS: Six groups were divided according to the concentration of TBAEMA incorporated to acrylic resin (Lucitone 550): 0, 0.5, 1.0, 1.5, 1.75 and 2%. Specimens surface were evaluated by Electron Spectroscopy for Chemical Analysis (ESCA) to detect the presence of amino groups, represented by nitrogen ratios. Flexural strength of the specimens was tested and results were analyzed by ANOVA and Tukey's test (α=0.05). RESULTS: Different nitrogen ratios were observed on specimen surfaces: 0, 0.13, 0.74, 0.66, 0.92 and 0.33% for groups 0, 0.5, 1.0, 1.5, 1.75, and 2%, respectively. Significant differences were found for flexural strength (p<0.001). The mean flexural strength values were 98.3±3.9, 93.3±3.2, 83.9±2.1, 82.8±5.2, 71.2±5.1 and 17.3±3.2 MPa for groups 0, 0.5, 1.0, 1.5, 1.75, and 2%, respectively. CONCLUSION: Within the limitations of this study, the incorporation of TBAEMA results in the presence of the potentially antimicrobial amino groups on specimen surfaces, but affect the flexural strength, depending on the concentration of TBAEMA.

Despite the large number of studies addressing the effect of microwave polymerization on the properties of acrylic resin, this method has received limited clinical acceptance. This study evaluated the influence of microwave polymerization on the flexural strength of a denture base resin. A conventional heat-polymerized (Clássico), a microwave-polymerized (Onda-Cryl) and a autopolymerizing acrylic (Jet) resins were used. Five groups were established, according to polymerization cycles: A, B and C (Onda-Cryl, short cycle - 500W/3 min, long - 90W/13 min + 500W/90 sec, and manufacturing microwave cycle - 320W/3 min + 0W/3 min + 720W/3 min); T (Clássico, water bath cycle - 74ºC/9h) and Q (Jet, press chamber cycle - 50ºC/15 min at 2 bar). Ten specimens (65 x 10 x 3.3mm) were prepared for each cycle. The flexural strength of the five groups was measured using a three-point bending test at a cross-head speed of 5 mm/min. Flexural strength values were analyzed by one-way ANOVA and the Tukey's test was performed to identify the groups that were significantly different at 5% level. The microwave-polymerized groups showed the highest means (p<0.05) for flexural strength (MPa) (A = 106.97 ± 5.31; B = 107.57 ± 3.99; C = 109.63 ± 5.19), and there were no significant differences among them. The heat-polymerized group (T) showed the lowest flexural strength means (84.40 ± 1.68), and differ significantly from all groups. The specimens of a microwavable denture base resin could be polymerized by different microwave cycles without risk of decreasing the flexural strength.

A resistência de união entre dente artificial e resina acrílica para base protética foi avaliada sob a influência de duas marcas comerciais de dentes artificiais (Biotone e Trilux) e de três resinas acrílicas, sendo duas polimerizadas convencionalmente em banho de água (QC-20 e Lucitone 550) e uma resina polimerizada por meio da energia de microondas (Acron-MC). As avaliações foram realizadas por meio de um ensaio mecânico de cisalhamento através da aplicação de uma carga perpendicular à interface dente-resina. Os resultados indicaram que, para a mesma resina, a resistência foi semelhante, independentemente do tipo de dente utilizado. Para os dois tipos de dente avaliados, as resinas Acron MC e Lucitone 550 apresentaram valores de resistência de união entre dente artificial e resina acrílica estatisticamente semelhantes e superiores em relação à resina QC-20.

Shear bond strength between artificial acrylic resin teeth and denture base resin was evaluated under the influence of two brands of artificial teeth (Biotone and Trilux) and three denture base resins. Two of these resins were conventionally polymerized in water bath (QC-20 and Lucitone 550), while the other was a microwave-polymerized resin (Acron-MC). The evaluations were done by means of a shear bond strength test with application of a perpendicular load to the interface tooth-resin. The results showed that, for the same denture resin, the strength was similar regardless of the tooth brand. Also, for the two evaluated brands of tooth, the resins Acron MC and Lucitone 550 presented similar shear bond strengths, which were statistically higher than for resin QC-20.